CEM-004 –Termodinâmica dos Sólidos – 1° semestre 2015. WJ Botta F.
Lista de exercícios / roteiro de estudos (8) 19/05/2015
1. Components A and B form a regular solution in the solid state for which ΔHm is 20.000XAXB
J/mol. At a temperature of 1000 K, calculate the composition of α' and α" in equilibrium and the
composition of the inflection points.
2. For the problem above calculate the temperature for immiscibility for a solution in which
XB=0,3.
3. Draw schematically free energy
versus composition diagrams for the
Ag- Pt peritectic diagram at
T= 1300 °C, 1100 °C and 900 °C.
4. Components A and B have melting temperatures of 1000 K and 900 K, respectively. Regular
solutions form with ΔHm equal to (20.000/T)XAXB and (200.000/T)XAXB J/mol in the liquid and
solid states, respectively. The enthalpies of fusion are 6000 J/mol and 5200 J/mol for A and B,
respectively. (a) Will a minimum occur in the solidus and liquidus ? (b) If so, calculate the
temperature of the minimum.
5. Descreva como obter ΔGm para soluções poliméricas,
identificando as principais diferenças em relação às
soluções regulares e discutindo as possíveis consequências
em termos de comportamento termodinâmico.
6. Utilize o diagrama polímero – solvente apresentado ao
lado para discutir todas as características químicas,
termodinâmicas e de transformações de fases associadas à
decomposição espinodal.